Nor is this kind of Grain, as I may call it, peculiar to Glass drops thus quenched; for (not to mention Coperas-stones, and divers other Marchasites and Minerals, which I have often taken notice of to be in the very same manner flaked or grained, with a kind of Pith in the middle) I have observed the same in all manner of cast Iron, especially the coarser sort, such as Stoves, and Furnaces, and Backs, and Pots are made of: For upon the breaking of any of those Substances it is obvious to observe, how from the out-sides towards the middle, there is a kind of Radiation or Grain much resembling this of the Glass-drop; but this Grain is most conspicuous in Iron-bullets, if they be broken: the same Phænomena may be produced by casting regulus of Antimony into a Bullet-mold, as also with Glass of Antimony, or with almost any such kind of Vitrified substance, either cast into a cold Mold or poured into Water.
Others of these Drops I heat red hot in the fire, and then suffered them to cool by degrees. And these I found to have quite lost all their fulminating or flying quality, as also their hard, brittle and springy texture; and to emerge of a much softer temper, and much easier to be broken or snapt with ones finger; but its strong and brittle quality was quite destroyed, and it seemed much of the same consistence with other green Glass well nealed in the Oven.
The Figure and bigness of these for the most part was the same with that of the Figure Z; that is, all the surface of them was very smooth and polisht, and for the most part round, but very rugged or knobbed about D, and all the length of the stem was here and there pitted or flatted. About D, which is at the upper part of the drop under that side of the stem which is concave, there usually was made some one or more little Hillocks or Prominences. The drop it self, before it be broken, appears very transparent, and towards the middle of it, to be very full of small Bubbles, of some kind of aerial substance, which by the refraction of the outward surface appear much bigger then really they are, and this may be in good part removed, by putting the drop under the surface of clear Water, for by that means most part of the refraction of the convex Surface of the drop is destroyed, and the bubbles will appear much smaller. And this, by the by, minds me of the appearing magnitude of the aperture of the iris, or pupil of the eye, which though it appear, and be therefore judged very large, is yet not above a quarter of the bigness it appears of, by the lenticular refraction of the Cornea.
The cause of all which Phænomena I imagine to be no other then this, That the Parts of the Glass being by the excessive heat of the fire kept off and separated one from another, and thereby put into a kind of sluggish fluid consistence, are suffered to drop off with that heat or agitation remaining in them, into cold Water; by which means the outsides of the drop are presently cool'd and crusted, and are thereby made of a loose texture, because the parts of it have not time to settle themselves leisurely together, and so to lie very close together: And the innermost parts of the drop, retaining still much of their former heat and agitations, remain